Used As Protective Packaging
- Used By Electronic And Automobile Industries
- Majorly Used In Pouch Forms By Electronic, automobiles, Furnitures And Other Industries To - Protect Fragile.
- Climatic Hazards (moisture/Dust)
- Easy To Carry Easy To Dispense Easy To Store Easy To Display.
- Flexible & Light Weight Packaging, Easy For Packing And Un Packing
Basic Properties
- Water Absorption - 0.02% After 24 Hrs
- Chemical Resistance - Excellent
- Thermal Conductivity - Very Low
- Service Temperature - 8 Degree C + 60 Degree C
- Transparency - 90%
Other Properties
- Tensile Elongation At Break - More Than 200%
- Bursting Strength - More Than 2500kg./cm Cu
Technical Specification
Bubble Diameter - 10 Mm
Bubble Density - 8150 Nos/sq Mt.
Maximum Width – 2.0 Mt
Length Available - Upto 100 Mts.
Thickness - 250g / 280g / 320g / 350g / 400g / 450g / 500g / 520g / 560g / 600g
|
Grade Available
|
Dimension
|
Width
|
|
SL-Single Layers Rolls
|
1mm - 5mm
|
1500mm / 1250mm
|
|
LR-Laminated Rolls
|
5mm-12mm
|
1400mm/1250mm
|
|
LS-Laminated Sheets
|
15mm-100mm
|
1000/1250/400mm
|
|
HDXL-High Density
|
3mm-100mm
|
1250/1400/1500mm
|
|
HMHD-Laminates
|
1mm-3mm
|
1400mm/1250mm
|
|
AS-Antistatic Pink
|
1mm-100mm
|
1500mm/1450mm
|
|
Property
|
Value
|
Unit
|
|
Density
|
20-25
|
gms / M3
|
|
Elongation at Break
|
Transverse Dir
Machine Dir
|
42-75
80-125<
|
%
%
|
|
Tensile Strength at Break
|
Transverse Dir
Machine Dir
|
1.80-3.50
2.50-6.00
|
Kg/cm2
Kg/cm2
|
|
Compression Strength (at 10% deformation)
|
0.05-0.20
|
Kg/cm2
|
|
Compression Set
|
10 Max
|
%
|
|
Water Absorption After 96 hours at 27°C
|
0.01-0.05
|
% by vol
|
|
Working Temperature
|
(-) 30 to (+) 70
|
°C
|
|
Thermal Conductivity (At 0°C mean Temp. Depending upon density)
|
0.025 – 0.032
|
K,cak / M har °C
|
|
Tear Strength
|
150 (Min)
|
GMF
|
|
Buoyancy
|
920
|
Kg
|
|
Surface Resistivity
|
108 - 1012
|
Ohms / sq mt 2
|
|